Electrochemical Corrosion and Mechanical properties of welded AA 6061 joined by TIG and MIG welding methods

E., MAHDI and E. O., ELTAI (2014) Electrochemical Corrosion and Mechanical properties of welded AA 6061 joined by TIG and MIG welding methods. In: International Conference on Future Trends In Mechanical, Production and Automation Engineering - FTMPAE 2014, 03- 04 May, 2014, International Conference on Future Trends In Mechanical, Production and Automation Engineering - FTMPAE 2014.

[img]
Preview
Text
20140620_113726.pdf - Published Version

Download (947kB) | Preview
Official URL: https://www.seekdl.org/conferences/paper/details/3...

Abstract

Aluminium alloy 6061 T6 circular specimens were joined using TIG and MIG welding methods. Heat Affected Zone (HAZ) and Base Metal (BM) were separated from each other. Potentiodynamic polarization and open circuit potential were employed to investigate the corrosion properties. Mechanical properties were evaluated using tensile, and hardness tests. It was shown that corrosion resistance was less for the HAZ of TIG and MIG welded specimens. The BM showed better corrosion resistance. The corrosion potential of HAZs was largely fluctuated; the corrosion potential for BM was relatively stable. Both welding procedures affected the mechanical properties of the specimens. The ultimate tensile strength of the TIG welded AA 6061 T6 specimens was 193.107 MPa which is 54% that of the base metal. The ultimate tensile strength of the MIG welded AA 6061 T6 specimens was 155.725 MPa which is less than 50% that of the BM. The HAZ of TIG welded specimens had the lowest hardness, for MIG welding the welded zone was shown to have the lowest hardness values due to the presence of pores which confirm using Scanning Electron Microscopy (SEM).

Item Type: Conference or Workshop Item (Paper)
Uncontrolled Keywords: TIG, MIG, Potentiodynamic, Scanning Electron Microscopy, Mechanical properties
Depositing User: Mr. John Steve
Date Deposited: 15 May 2019 12:33
Last Modified: 15 May 2019 12:33
URI: http://publications.theired.org/id/eprint/2353

Actions (login required)

View Item View Item